ABC3_oP40_17_abcd_2e_abcd4e & a,b/a,c/a,x1,x2,x3,x4,y5,y6,y7,y8,x9,y9,z9,x10,y10,z10,x11,y11,z11,x12,y12,z12,x13,y13,z13,x14,y14,z14 --params=5.504,1.01162790698,2.81976744186,0.481,-0.025,0.019,0.525,0.519,0.025,-0.019,0.475,0.014,0.005,0.375,0.514,0.505,0.375,0.25,0.25,0.375,0.75,0.25,0.375,0.25,0.75,0.375,0.75,0.75,0.375 & P222_{1} D_{2}^{2} #17 (a^2b^2c^2d^2e^6) & oP40 & None & NaNbO3 & NaNbO3 & P. Vousden, Acta Cryst. 4, 545-551 (1951) 1.00000000000000 5.50400000000000 0.00000000000000 0.00000000000000 0.00000000000000 5.56800000000000 0.00000000000000 0.00000000000000 0.00000000000000 15.52000000000000 Na Nb O 8 8 24 Direct 0.48100000000000 0.00000000000000 0.00000000000000 Na (2a) -0.48100000000000 0.00000000000000 0.50000000000000 Na (2a) 0.01900000000000 0.50000000000000 0.00000000000000 Na (2b) -0.01900000000000 0.50000000000000 0.50000000000000 Na (2b) 0.00000000000000 0.51900000000000 0.25000000000000 Na (2c) 0.00000000000000 -0.51900000000000 0.75000000000000 Na (2c) 0.50000000000000 -0.01900000000000 0.25000000000000 Na (2d) 0.50000000000000 0.01900000000000 0.75000000000000 Na (2d) 0.01400000000000 0.00500000000000 0.37500000000000 Nb (4e) -0.01400000000000 -0.00500000000000 0.87500000000000 Nb (4e) -0.01400000000000 0.00500000000000 0.12500000000000 Nb (4e) 0.01400000000000 -0.00500000000000 -0.37500000000000 Nb (4e) 0.51400000000000 0.50500000000000 0.37500000000000 Nb (4e) -0.51400000000000 -0.50500000000000 0.87500000000000 Nb (4e) -0.51400000000000 0.50500000000000 0.12500000000000 Nb (4e) 0.51400000000000 -0.50500000000000 -0.37500000000000 Nb (4e) -0.02500000000000 0.00000000000000 0.00000000000000 O (2a) 0.02500000000000 0.00000000000000 0.50000000000000 O (2a) 0.52500000000000 0.50000000000000 0.00000000000000 O (2b) -0.52500000000000 0.50000000000000 0.50000000000000 O (2b) 0.00000000000000 0.02500000000000 0.25000000000000 O (2c) 0.00000000000000 -0.02500000000000 0.75000000000000 O (2c) 0.50000000000000 0.47500000000000 0.25000000000000 O (2d) 0.50000000000000 -0.47500000000000 0.75000000000000 O (2d) 0.25000000000000 0.25000000000000 0.37500000000000 O (4e) -0.25000000000000 -0.25000000000000 0.87500000000000 O (4e) -0.25000000000000 0.25000000000000 0.12500000000000 O (4e) 0.25000000000000 -0.25000000000000 -0.37500000000000 O (4e) 0.75000000000000 0.25000000000000 0.37500000000000 O (4e) -0.75000000000000 -0.25000000000000 0.87500000000000 O (4e) -0.75000000000000 0.25000000000000 0.12500000000000 O (4e) 0.75000000000000 -0.25000000000000 -0.37500000000000 O (4e) 0.25000000000000 0.75000000000000 0.37500000000000 O (4e) -0.25000000000000 -0.75000000000000 0.87500000000000 O (4e) -0.25000000000000 0.75000000000000 0.12500000000000 O (4e) 0.25000000000000 -0.75000000000000 -0.37500000000000 O (4e) 0.75000000000000 0.75000000000000 0.37500000000000 O (4e) -0.75000000000000 -0.75000000000000 0.87500000000000 O (4e) -0.75000000000000 0.75000000000000 0.12500000000000 O (4e) 0.75000000000000 -0.75000000000000 -0.37500000000000 O (4e)