AB3C6_cI80_206_b_d_e & a,x2,x3,y3,z3 --params=9.4,-0.0344,0.338,0.1,0.125 & Ia(-3) T_h^3 #206 (bde) & cI80 & D5_3 & (Mn,Fe)2O3 & Bixbyite & H. Dachs, Zeitschrift f\"{u}r Kristallographie - Crystalline Materials, 107, 370-395 (1956) 1.0000000000000000 -4.70000000000000 4.70000000000000 4.70000000000000 4.70000000000000 -4.70000000000000 4.70000000000000 4.70000000000000 4.70000000000000 -4.70000000000000 Fe Mn O 4 12 24 Direct 0.00000000000000 0.00000000000000 -0.50000000000000 Fe (8b) 0.00000000000000 -0.50000000000000 0.00000000000000 Fe (8b) -0.50000000000000 0.00000000000000 0.00000000000000 Fe (8b) 0.50000000000000 0.50000000000000 0.50000000000000 Fe (8b) -0.03440000000000 0.25000000000000 0.21560000000000 Mn (24d) 0.03440000000000 0.75000000000000 0.78440000000000 Mn (24d) 0.21560000000000 -0.03440000000000 0.25000000000000 Mn (24d) 0.25000000000000 0.21560000000000 -0.03440000000000 Mn (24d) 0.25000000000000 0.71560000000000 0.46560000000000 Mn (24d) 0.46560000000000 0.25000000000000 0.71560000000000 Mn (24d) 0.53440000000000 0.75000000000000 1.28440000000000 Mn (24d) 0.71560000000000 0.46560000000000 0.25000000000000 Mn (24d) 0.75000000000000 0.78440000000000 0.03440000000000 Mn (24d) 0.75000000000000 1.28440000000000 0.53440000000000 Mn (24d) 0.78440000000000 0.03440000000000 0.75000000000000 Mn (24d) 1.28440000000000 0.53440000000000 0.75000000000000 Mn (24d) 0.03700000000000 0.26200000000000 0.97500000000000 O (48e) -0.03700000000000 -0.26200000000000 -0.97500000000000 O (48e) 0.06200000000000 0.52500000000000 0.78700000000000 O (48e) -0.06200000000000 -0.52500000000000 -0.78700000000000 O (48e) 0.22500000000000 0.46300000000000 0.43800000000000 O (48e) -0.22500000000000 -0.46300000000000 -0.43800000000000 O (48e) 0.26200000000000 0.97500000000000 0.03700000000000 O (48e) -0.26200000000000 -0.97500000000000 -0.03700000000000 O (48e) 0.27500000000000 0.71300000000000 1.23800000000000 O (48e) -0.27500000000000 -0.71300000000000 -1.23800000000000 O (48e) 0.43800000000000 0.22500000000000 0.46300000000000 O (48e) -0.43800000000000 -0.22500000000000 -0.46300000000000 O (48e) 0.46300000000000 0.43800000000000 0.22500000000000 O (48e) -0.46300000000000 -0.43800000000000 -0.22500000000000 O (48e) 0.52500000000000 0.78700000000000 0.06200000000000 O (48e) -0.52500000000000 -0.78700000000000 -0.06200000000000 O (48e) 0.71300000000000 1.23800000000000 0.27500000000000 O (48e) -0.71300000000000 -1.23800000000000 -0.27500000000000 O (48e) 0.78700000000000 0.06200000000000 0.52500000000000 O (48e) -0.78700000000000 -0.06200000000000 -0.52500000000000 O (48e) 0.97500000000000 0.03700000000000 0.26200000000000 O (48e) -0.97500000000000 -0.03700000000000 -0.26200000000000 O (48e) 1.23800000000000 0.27500000000000 0.71300000000000 O (48e) -1.23800000000000 -0.27500000000000 -0.71300000000000 O (48e)