AB2C8D_oP24_49_g_q_2qr_e & a,b/a,c/a,x3,y3,x4,y4,x5,y5,x6,y6,z6 --params=6.3302356554,1.0,1.50710900473,0.5184,0.7996,0.258,-0.0697,0.3652,0.6307,0.2617,0.1943,0.8286 & Pccm D_{2h}^{3} #49 (egq^3r) & oP24 & None & CsPr[MoO4]2 & & V. A. Vinokurov and P. V. Klevtsov, Sov. Phys. Crystallogr. 17, 102-106 (1972) 1.00000000000000 6.33023565540000 0.00000000000000 0.00000000000000 0.00000000000000 6.33023565540000 0.00000000000000 0.00000000000000 0.00000000000000 9.54035515830000 Cs Mo O Pr 2 4 16 2 Direct 0.00000000000000 0.50000000000000 0.25000000000000 Cs (2g) 0.00000000000000 0.50000000000000 0.75000000000000 Cs (2g) 0.51840000000000 0.79960000000000 0.00000000000000 Mo (4q) -0.51840000000000 -0.79960000000000 0.00000000000000 Mo (4q) -0.51840000000000 0.79960000000000 0.50000000000000 Mo (4q) 0.51840000000000 -0.79960000000000 0.50000000000000 Mo (4q) 0.25800000000000 -0.06970000000000 0.00000000000000 O (4q) -0.25800000000000 0.06970000000000 0.00000000000000 O (4q) -0.25800000000000 -0.06970000000000 0.50000000000000 O (4q) 0.25800000000000 0.06970000000000 0.50000000000000 O (4q) 0.36520000000000 0.63070000000000 0.00000000000000 O (4q) -0.36520000000000 -0.63070000000000 0.00000000000000 O (4q) -0.36520000000000 0.63070000000000 0.50000000000000 O (4q) 0.36520000000000 -0.63070000000000 0.50000000000000 O (4q) 0.26170000000000 0.19430000000000 0.82860000000000 O (8r) -0.26170000000000 -0.19430000000000 0.82860000000000 O (8r) -0.26170000000000 0.19430000000000 -0.32860000000000 O (8r) 0.26170000000000 -0.19430000000000 -0.32860000000000 O (8r) -0.26170000000000 -0.19430000000000 -0.82860000000000 O (8r) 0.26170000000000 0.19430000000000 -0.82860000000000 O (8r) 0.26170000000000 -0.19430000000000 1.32860000000000 O (8r) -0.26170000000000 0.19430000000000 1.32860000000000 O (8r) 0.00000000000000 0.00000000000000 0.25000000000000 Pr (2e) 0.00000000000000 0.00000000000000 0.75000000000000 Pr (2e)