A8B_tI18_139_deh_a & a,c/a,z3,x4 --params=5.71361,1.10055114017,0.2922,0.24433 & I4/mmm D_{4h}^{17} #139 (adeh) & tI18 & $D2_{g}$ & Fe8N & Fe8N & S. Yamashita et al., J. Solid State Chem. 194, 76-79 (2012) 1.00000000000000 -2.85680500000000 2.85680500000000 3.14406000000000 2.85680500000000 -2.85680500000000 3.14406000000000 2.85680500000000 2.85680500000000 -3.14406000000000 Fe N 8 1 Direct 0.75000000000000 0.25000000000000 0.50000000000000 Fe (4d) 0.25000000000000 0.75000000000000 0.50000000000000 Fe (4d) 0.29220000000000 0.29220000000000 0.00000000000000 Fe (4e) -0.29220000000000 -0.29220000000000 0.00000000000000 Fe (4e) 0.24433000000000 0.24433000000000 0.48866000000000 Fe (8h) -0.24433000000000 -0.24433000000000 -0.48866000000000 Fe (8h) 0.24433000000000 -0.24433000000000 0.00000000000000 Fe (8h) -0.24433000000000 0.24433000000000 0.00000000000000 Fe (8h) 0.00000000000000 0.00000000000000 0.00000000000000 N (2a)