A6B_oC28_63_efg_c & a,b/a,c/a,y1,x2,y3,z3,x4,y4 --params=7.5551,0.860266574896,1.17435904224,0.45686,0.32602,0.13917,0.10039,0.31768,0.28622 & Cmcm D_{2h}^{17} #63 (cefg) & oC28 & $D2_{h}$ & MnAl6 & MnAl6 & A. Kontio and P. Coppens, Acta Crystallogr. Sect. B Struct. Sci. 37, 433-435 (1981) 1.00000000000000 3.77755000000000 -3.24970000000000 0.00000000000000 3.77755000000000 3.24970000000000 0.00000000000000 0.00000000000000 0.00000000000000 8.87240000000000 Al Mn 12 2 Direct 0.32602000000000 0.32602000000000 0.00000000000000 Al (8e) -0.32602000000000 -0.32602000000000 0.50000000000000 Al (8e) -0.32602000000000 -0.32602000000000 0.00000000000000 Al (8e) 0.32602000000000 0.32602000000000 0.50000000000000 Al (8e) -0.13917000000000 0.13917000000000 0.10039000000000 Al (8f) 0.13917000000000 -0.13917000000000 0.60039000000000 Al (8f) -0.13917000000000 0.13917000000000 0.39961000000000 Al (8f) 0.13917000000000 -0.13917000000000 -0.10039000000000 Al (8f) 0.03146000000000 0.60390000000000 0.25000000000000 Al (8g) -0.03146000000000 -0.60390000000000 0.75000000000000 Al (8g) -0.60390000000000 -0.03146000000000 0.25000000000000 Al (8g) 0.60390000000000 0.03146000000000 0.75000000000000 Al (8g) -0.45686000000000 0.45686000000000 0.25000000000000 Mn (4c) 0.45686000000000 -0.45686000000000 0.75000000000000 Mn (4c)