A6B2C_tP18_128_eh_d_a & a,c/a,z3,x4,y4 --params=7.057532571,1.41383170154,0.2523,0.2217,0.2511 & P4/mnc D_{4h}^{6} #128 (adeh) & tP18 & None & K2SnCl6 & & H. Boysen and A. W. Hewat, Acta Crystallogr. Sect. B Struct. Sci. 34, 1412-1418 (1978) 1.00000000000000 7.05753257100000 0.00000000000000 0.00000000000000 0.00000000000000 7.05753257100000 0.00000000000000 0.00000000000000 0.00000000000000 9.97816328350000 Cl K Sn 12 4 2 Direct 0.00000000000000 0.00000000000000 0.25230000000000 Cl (4e) 0.50000000000000 0.50000000000000 0.24770000000000 Cl (4e) 0.00000000000000 0.00000000000000 -0.25230000000000 Cl (4e) 0.50000000000000 0.50000000000000 0.75230000000000 Cl (4e) 0.22170000000000 0.25110000000000 0.00000000000000 Cl (8h) -0.22170000000000 -0.25110000000000 0.00000000000000 Cl (8h) -0.25110000000000 0.22170000000000 0.00000000000000 Cl (8h) 0.25110000000000 -0.22170000000000 0.00000000000000 Cl (8h) 0.27830000000000 0.75110000000000 0.50000000000000 Cl (8h) 0.72170000000000 0.24890000000000 0.50000000000000 Cl (8h) 0.75110000000000 0.72170000000000 0.50000000000000 Cl (8h) 0.24890000000000 0.27830000000000 0.50000000000000 Cl (8h) 0.00000000000000 0.50000000000000 0.25000000000000 K (4d) 0.50000000000000 0.00000000000000 0.25000000000000 K (4d) 0.00000000000000 0.50000000000000 0.75000000000000 K (4d) 0.50000000000000 0.00000000000000 0.75000000000000 K (4d) 0.00000000000000 0.00000000000000 0.00000000000000 Sn (2a) 0.50000000000000 0.50000000000000 0.50000000000000 Sn (2a)