A3B2_cI40_220_d_c & a,x1,x2 --params=8.135,0.0492,0.2896 & I(-4)3d T_d^6 #220 (cd) & cI40 & D5_c & Pu2C3 & & J.L. Green, G.P. Arnold, J.A. Leary and N.G. Nereson, J. Nucl. Mater. 34, 281-289 (1970) 1.0000000000000000 -4.06750000000000 4.06750000000000 4.06750000000000 4.06750000000000 -4.06750000000000 4.06750000000000 4.06750000000000 4.06750000000000 -4.06750000000000 C Pu 12 8 Direct -0.03960000000000 0.21040000000000 0.75000000000000 C (24d) 0.03960000000000 0.75000000000000 0.78960000000000 C (24d) 0.21040000000000 0.75000000000000 -0.03960000000000 C (24d) 0.25000000000000 0.53960000000000 0.28960000000000 C (24d) 0.25000000000000 0.71040000000000 0.46040000000000 C (24d) 0.28960000000000 0.25000000000000 0.53960000000000 C (24d) 0.46040000000000 0.25000000000000 0.71040000000000 C (24d) 0.53960000000000 0.28960000000000 0.25000000000000 C (24d) 0.71040000000000 0.46040000000000 0.25000000000000 C (24d) 0.75000000000000 -0.03960000000000 0.21040000000000 C (24d) 0.75000000000000 0.78960000000000 0.03960000000000 C (24d) 0.78960000000000 0.03960000000000 0.75000000000000 C (24d) 0.00000000000000 -0.09840000000000 0.50000000000000 Pu (16c) 0.00000000000000 0.40160000000000 0.50000000000000 Pu (16c) 0.09840000000000 0.09840000000000 0.09840000000000 Pu (16c) -0.09840000000000 0.50000000000000 0.00000000000000 Pu (16c) 0.40160000000000 0.50000000000000 0.00000000000000 Pu (16c) 0.50000000000000 0.00000000000000 -0.09840000000000 Pu (16c) 0.50000000000000 0.00000000000000 0.40160000000000 Pu (16c) 0.59840000000000 0.59840000000000 0.59840000000000 Pu (16c)