A3B10_cI52_229_e_fh & a,x1,x2,y3 --params=8.9822,0.3538,0.13505,0.3045 & Im-3m O_{h}^{9} #229 (efh) & cI52 & $D8_{1}$ & Fe3Zn10 & $\gamma$-brass Fe$_{3}$Zn$_{10}$ & J. Schramm, Z. Metallkd. 30, 122-130 (1938) 1.00000000000000 -4.49110000000000 4.49110000000000 4.49110000000000 4.49110000000000 -4.49110000000000 4.49110000000000 4.49110000000000 4.49110000000000 -4.49110000000000 Fe Zn 6 20 Direct 0.00000000000000 0.35380000000000 0.35380000000000 Fe (12e) 0.00000000000000 -0.35380000000000 -0.35380000000000 Fe (12e) 0.35380000000000 0.00000000000000 0.35380000000000 Fe (12e) -0.35380000000000 0.00000000000000 -0.35380000000000 Fe (12e) 0.35380000000000 0.35380000000000 0.00000000000000 Fe (12e) -0.35380000000000 -0.35380000000000 0.00000000000000 Fe (12e) 0.27010000000000 0.27010000000000 0.27010000000000 Zn (16f) 0.00000000000000 0.00000000000000 -0.27010000000000 Zn (16f) 0.00000000000000 -0.27010000000000 0.00000000000000 Zn (16f) -0.27010000000000 0.00000000000000 0.00000000000000 Zn (16f) 0.00000000000000 0.00000000000000 0.27010000000000 Zn (16f) -0.27010000000000 -0.27010000000000 -0.27010000000000 Zn (16f) 0.00000000000000 0.27010000000000 0.00000000000000 Zn (16f) 0.27010000000000 0.00000000000000 0.00000000000000 Zn (16f) 0.60900000000000 0.30450000000000 0.30450000000000 Zn (24h) 0.00000000000000 0.30450000000000 -0.30450000000000 Zn (24h) 0.00000000000000 -0.30450000000000 0.30450000000000 Zn (24h) -0.60900000000000 -0.30450000000000 -0.30450000000000 Zn (24h) 0.30450000000000 0.60900000000000 0.30450000000000 Zn (24h) -0.30450000000000 0.00000000000000 0.30450000000000 Zn (24h) 0.30450000000000 0.00000000000000 -0.30450000000000 Zn (24h) -0.30450000000000 -0.60900000000000 -0.30450000000000 Zn (24h) 0.30450000000000 0.30450000000000 0.60900000000000 Zn (24h) 0.30450000000000 -0.30450000000000 0.00000000000000 Zn (24h) -0.30450000000000 0.30450000000000 0.00000000000000 Zn (24h) -0.30450000000000 -0.30450000000000 -0.60900000000000 Zn (24h)