A2B_oP24_61_2c_c & a,b/a,c/a,x1,y1,z1,x2,y2,z2,x3,y3,z3 --params=15.035,0.363418689724,0.372929830396,0.028,0.634,0.171,0.168,0.221,0.081,0.1181,0.0252,0.3378 & Pbca D_{2h}^{15} #61 (c^3) & oP24 & $C52$ & O2Te & Tellurite & H. Beyer, Zeitschrift f{"u}r Kristallographie - Crystalline Materials 124, 228-237 (1967) 1.00000000000000 15.03500000000000 0.00000000000000 0.00000000000000 0.00000000000000 5.46400000000000 0.00000000000000 0.00000000000000 0.00000000000000 5.60700000000000 O Te 16 8 Direct 0.02800000000000 0.63400000000000 0.17100000000000 O (8c) 0.47200000000000 -0.63400000000000 0.67100000000000 O (8c) -0.02800000000000 1.13400000000000 0.32900000000000 O (8c) 0.52800000000000 -0.13400000000000 -0.17100000000000 O (8c) -0.02800000000000 -0.63400000000000 -0.17100000000000 O (8c) 0.52800000000000 0.63400000000000 0.32900000000000 O (8c) 0.02800000000000 -0.13400000000000 0.67100000000000 O (8c) 0.47200000000000 1.13400000000000 0.17100000000000 O (8c) 0.16800000000000 0.22100000000000 0.08100000000000 O (8c) 0.33200000000000 -0.22100000000000 0.58100000000000 O (8c) -0.16800000000000 0.72100000000000 0.41900000000000 O (8c) 0.66800000000000 0.27900000000000 -0.08100000000000 O (8c) -0.16800000000000 -0.22100000000000 -0.08100000000000 O (8c) 0.66800000000000 0.22100000000000 0.41900000000000 O (8c) 0.16800000000000 0.27900000000000 0.58100000000000 O (8c) 0.33200000000000 0.72100000000000 0.08100000000000 O (8c) 0.11810000000000 0.02520000000000 0.33780000000000 Te (8c) 0.38190000000000 -0.02520000000000 0.83780000000000 Te (8c) -0.11810000000000 0.52520000000000 0.16220000000000 Te (8c) 0.61810000000000 0.47480000000000 -0.33780000000000 Te (8c) -0.11810000000000 -0.02520000000000 -0.33780000000000 Te (8c) 0.61810000000000 0.02520000000000 0.16220000000000 Te (8c) 0.11810000000000 0.47480000000000 0.83780000000000 Te (8c) 0.38190000000000 0.52520000000000 0.33780000000000 Te (8c)